When I moved in two years ago, the plumbing in this area showed significant corrosion. There was no galvanic isolation between the steel pipes leading to the upstairs bath, and the copper piping in the basement. I updated the entire thing to what is shown below (cold water stack is labeled -- the hot water stack to the left is identical).

The two valves at the bottom (shutoff for laundry sink) failed last month -- the cold one broke off in my hand when I needed to close it to work on the laundry sink. When I replaced it I noticed that the hot water side was leaking. This one failed when I went to remove it (luckily water was off). Both valves failed at a joint in the valve that appeared pressed together, and showed some signs of corrosion inside.

You can see that the threaded nipples below the valves show some corrosion. I assumed this was due to the leaking valves. I also assumed the valves failed due to a faulty design of the pressed joint. But to avoid having to do this repair again in the future, I want to confirm if this set-up did/will result in galvanic corrosion, or if I was just unlucky in choosing a poorly designed valve.

If it's relevant, I am in Wisconsin on city water, and both hot and cold water are softened.

When I moved in two years ago, the plumbing in this area showed significant corrosion. There was no galvanic isolation between the steel pipes leading to the upstairs bath, and the copper piping in the basement. I updated the entire thing to what is shown below (cold water stack is labeled -- the hot water stack to the left is identical).

The two valves at the bottom (shutoff for laundry sink) failed last month, the cold one broke off in my hand when I needed to close it to work on the laundry sink. When I replaced it I noticed that the hot water side was leaking, this one failed when I went to remove it (luckily water was off). Both valves failed at a joint in the valve that appeared pressed together, and showed some signs of corrosion inside.

In the photos below you can see that the threaded nipples below the valves show some corrosion. I assumed this was due to the leaking valves. I also assumed the valves failed due to a faulty design of the pressed joint. But to avoid having to do this repair again in the future, I want to confirm if this set-up did/will result in galvanic corrosion, or if I was just unlucky in choosing a poorly designed valve.

If it's relevant, I am in Wisconsin on city water, and both hot and cold water are softened.